Product  Name

1018 Cold  Rolled Steel Coil

Production  Process

Hot Rolling,  Cold Rolling

Material  Standards

AISI, ASTM,  ASME, DIN, BS, EN, ISO, JIS, GOST, SAE, etc.

Width

100mm-3000mm

Length

1m-12m, or  Customized Size

Thickness

0.1mm-400mm

Delivery  Conditions

Rolling,  Annealing, Quenching, Tempered or Standard

Surface  Process

Ordinary, Wire  Drawing, Laminated Film

Element

Content (%)

Iron, Fe

99.31-99.7 %

Manganese, Mn

0.30-0.50  %

Carbon, C

0.10%

Sulfur, S

0.05%

Phosphorous, P

0.04%

Properties

Metric

Imperial

Tensile  strength

340 MPa

49300 psi

Yield strength (depending on temper)

285  MPa

41300  psi

Elastic modulus

190-210  Gpa

27557-30458  ksi

Bulk modulus (typical for steel)

200  GPa

29000  ksi

Shear modulus (typical for steel)

80.0  GPa

11600  ksi

Poisson’s ratio

0.27-0.30

0.27-0.30

Elongation at break (in 50 mm)

20%

20%

Reduction of area

45%

45%

Hardness, Brinell

95

95

Hardness, Knoop (converted from Brinell hardness)

113

113

Hardness, Rockwell B (converted from Brinell hardness)

55

55

Hardness, Vickers (converted from Brinell hardness)

98

98

Machinability (based on AISI 1212 steel as 100 machinability)

55

55

The  machinability of group I bar, rod, and wire products can be improved by cold  drawing)

AISI  1008 carbon steel is primarily used in extruded, cold headed, cold upset, and  cold pressed parts and forms.